Hydroxylation-induced modifications of the Al2O3/NiAl(0 0 1) surface at low water vapour pressure

STM, STS, LEED and XPS data for crystalline θ-Al₂O₃ and non-crystalline Al₂O₃ ultra-thin films grown on NiAl(0 0 1) at 1025 K and exposed to water vapour at low pressure (1 × 10⁻⁷-1 × 10⁻⁵ mbar) and room temperature are reported. Water dissociation is observed at low pressure. This reactivity is assigned to the presence of a high density of coordinatively unsaturated cationic sites at the surface of the oxide film. The hydroxyl/hydroxide groups cannot be directly identify by their XPS binding energy, which is interpreted as resulting from the high BE positions of the oxide anions (O_1s signal at 532.5-532.8 eV). However the XPS intensities give evidence of an uptake of oxygen accompanied by an increase of the surface coverage by Al³⁺ cations, and a decrease of the concentration in metallic Al at the alloy interface. A value of ∼2 for the oxygen to aluminium ions surface concentration ratio indicates the formation of an oxy-hydroxide (AlO_xOH_y with x + y ∼ 2) hydroxylation product. STM and LEED show the amorphisation and roughening of the oxide film. At P(H₂O) = 1 × 10⁻⁷ mbar, only the surface of the oxide film is modified, with formation of nodules of ∼2 nm lateral size covering homogeneously the surface. STS shows that essentially the valence band is modified with an increase of the density of states at the band edge. With increasing pressure, hydroxylation is amplified, leading to an increased coverage of the alloy by oxy-hydroxide products and to the formation of larger nodules (∼7 nm) of amorphous oxy-hydroxide. Roughening and loss of the nanostructure indicate a propagation of the reaction that modifies the bulk structure of the oxide film. Amorphisation can be reverted to crystallization by annealing under UHV at 1025 K when the surface of the oxide film has been modified, but not when the bulk structure has been modified.     

Stress State of Multilayer Thin-Walled Elements with Interfacial Defects of Structure

Based on the discrete-structural theory of thin plates and shells, a calculation model for thin-walled elements consisting of a number of rigid anisotropic layers is put forward. It is assumed that the transverse shear and compression stresses are equal on the interfaces. Elastic slippage is allowed over the interfaces between adjacent layers. The solution to the problem is obtained in a geometrically nonlinear statement with account of the influence of transverse shear and compression strains. The stress-strain state of circular two-layer transversely isotropic plates, both without defects and with a local area of adhesion failure at their center, is investigated numerically and experimentally. It is found that the kinematic and static contact conditions on the interfaces of layered thin-walled structural members greatly affect the magnitude of stresses and strains. With the use of three variants of calculation models, in the cases of perfect and weakened contact conditions between layers, the calculation results for circular plates are compared. It is revealed that the variant suggested in this paper adequately reflects the behavior of layered thin-walled structural elements under large deformations. __________ Translated from Mekhanika Kompozitnykh Materialov, Vol. 41, No. 6, pp. 761–772, November–December, 2005.     

Luminescence properties of anodic aluminum oxide films with organic luminophores embedded into pores

Luminescence properties of porous anodic aluminum oxide films formed in a 0.6 M solution of citric acid and luminescence of paraterphenyl, perylene, coumarin 7, and rhodamine 6G dyes adsorbed by the films are investigated. The nature of emitting centers in anodic aluminum oxide is revealed. Intense photoluminescence of all tested dyes embedded into pores of anodic aluminum oxide has been found. A redshift of fluorescence spectra of dyes adsorbed by the matrix and emergence of an additional longwave band have been detected. Data obtained can be used in developing new thin-film luminescent coatings for future applications in optoelectronics and molecular electronics. Translated from Zhurnal Prikladnoi Spektroskopii, Vol. 64, No 4, pp. 483–488, July–August, 1997.     

Luttinger liquid with asymmetric dispersion

We present an extension of the Tomonaga-Luttinger model in which left and right-moving particles have different Fermi velocities. We derive expressions for one-particle Green's functions, momentum-distributions, density of states, charge compressibility and conductivity as functions of both the velocity difference ε and the strength of the interaction β. This allows us to identify a novel restricted region in the parameter space in which the system keeps the main features of a Luttinger liquid but with an unusual behavior of the density of states and the static charge compressibility κ. In particular κ diverges on the boundary of the restricted region, indicating the occurrence of a phase transition. Received 20 May 2002 / Received in final form 23 August 2002 Published online 19 November 2002     

The 2D Rancieite-type manganic acid and its alkali-exchanged derivatives: Part I — Chemical characterization and thermal behavior

The 2D Rancieite type manganic acid was prepared by reduction of KMnO₄ in acidic medium. Its ion exchange behavior allows to prepare alkali derivatives. All compounds were characterized with use of a combination of X-ray diffraction, chemical analyses, TGA, magnetic measurements and spectroscopic techniques. The evolution of their chemical composition versus temperature was studied between 180 and 400 °C. It shows that the dehydration process is partly reversible in these compounds whereas the weak reduction is irreversible. The 2D Rancieite-type manganic acid is readily different from a Birnessite-type phyllomanganate, as shown by several features: the interlayer distance, the ion exchange capacity, the thermal behavior, the interlayer cation content, the manganese average oxidation state, the magnetic behavior and the IR spectrum.     

Heat-treatment studies of molybdenum oxide-monohydrate

The dehydration of molybdic acid, MoO₃---H₂O, was studied by thermal analysis, X-ray diffractometry and FTIR spectroscopy. The results show that an intermediate phase, MoO₃-2/3H₂O is formed at 216 °C and the monoclinic form of MoO₃ is grown above 350 °C. The mechanism of dehydration and structural rearrangement were confirmed by the features of the infrared spectra showing formation of corner-shared MoO₆ octahedra.     

Phase transfer of highly monodisperse iron oxide nanocrystals with Pluronic F127 for biomedical applications

Iron oxide nanoparticles made from the thermal decomposition method are highly uniform in all respects (size, shape, composition and crystallography), making them ideal candidates for many bioapplications. The surfactant coating on the as-synthesized nanoparticles renders the nanoparticles insoluble in aqueous solutions. For biological applications nanoparticles must be water soluble. Here we demonstrate the phase transfer of our nanoparticles with the biocompatible copolymer Pluronic F127. Transmission electron microscopy, Fourier transform infrared spectroscopy and dynamic light scattering indicate that the nanoparticles are coated discretely. Magnetic measurements show that the nanoparticles remain superparamagnetic with saturation magnetization ∼96% of the maximum theoretical value.     

A refined stress-strain analysis in the load transfer zone of flat specimens of high-strength unidirectional composites in uniaxial tension 1. Theoretical analysis

With the use of an analytical approach developed, the influence of distribution of a tangential load on the stress concentration in uniaxially tensioned flat specimens of high-strength unidirectional composites near the grips of a testing machine is evaluated. In view of singularity of the analytical solution derived at the points of discontinuity of boundary conditions, for estimating the stress concentration, it is suggested to employ the averaged value of longitudinal stresses, which is calculated by means of an improper integral across the thickness of a near-surface layer. __________ Translated from Mekhanika Kompozitnykh Materialov, Vol. 42, No. 6, pp. 787–796, November–December, 2006.     

Dextran-modified iron oxide nanoparticles

Dextran-modified iron oxide nanoparticles were prepared by precipitation of Fe（Ⅱ） and Fe（Ⅲ） salts with ammonium hydroxide by two methods. Iron oxide was precipitated either in the presence of dextran solution, or the dextran solution was added after precipitation. In the second method, the iron oxide particle size and size distribution could be controlled depending on the concentration of dextran in the solution. The nanoparticles were characterized by size-exclusion chromatography, transmission electron microscopy and dynamic light scattering. Optimal conditions for preparation of stable iron oxide colloid particles were determined, The dextran/iron oxide ratio 0-0,16 used in precipitation of iron salts can be recommended for synthesis of nanoparticles suitable for biomedical applications, as the colloid does not contain excess dextran and does not coagulate.